• Technical data sheet:
HM-180C3P ↓

• Application video:
Unidirectional carbon fiber for structural strengthening

• Brochure:
Horse FRP strengthening system ↓

• Software:
Horse FRP Software ↓

Documents Download

• Technical data sheet:
HM-180C3P ↓

• Application video:
Unidirectional carbon fiber for structural strengthening

• Brochure:
Horse FRP strengthening system ↓

• Software:
Horse FRP Software ↓

carbon fiber adhesive for structural strengthening

Characteristics of HM-180C3P Epoxy

• Good compatibility with carbon fiber;

• Strong penetration, can well infiltrate into the concrete surface;

• Aging, water resistance and chemical corrosion resistance, excellent performance;

• The adhesive layer has excellent physical mechanical properties after curing, strong toughness and a certain degree of elasticity.

Characteristics of HM-180C3P Epoxy

• Good compatibility with carbon fiber;

• Strong penetration, can well infiltrate into the concrete surface;

• Aging, water resistance and chemical corrosion resistance, excellent performance;

• The adhesive layer has excellent physical mechanical properties after curing, strong toughness and a certain degree of elasticity.

carbon fiber adhesive for structural strengthening
carbon fiber adhesive for structural strengthening

Application Range

• Used as structural resin in carbon fiber strengthening system.

• Reinforce the substrate concrete after chiseled;

• In order to improve work efficiency of the carbon fiber with concrete, can close the concrete substrate small holes.

• This product is epoxy fiber adhesive of high performance, can be used for the effective penetration bonding between many substrate materials such as concrete, steel material, ceramic, stone, wood component and many fiber fabrics such as carbon fiber, glass fiber, basalt fiber, aramid fiber.

• It is mainly used for the strengthening and reinforcement of buildings.

carbon fiber adhesive for structural strengthening

Application Range

• Used as structural resin in carbon fiber strengthening system.

• Reinforce the substrate concrete after chiseled;

• In order to improve work efficiency of the carbon fiber with concrete, can close the concrete substrate small holes.

• This product is epoxy fiber adhesive of high performance, can be used for the effective penetration bonding between many substrate materials such as concrete, steel material, ceramic, stone, wood component and many fiber fabrics such as carbon fiber, glass fiber, basalt fiber, aramid fiber.

• It is mainly used for the strengthening and reinforcement of buildings.

carbon fiber adhesive for FRP strengthening

Transportation and Storage

• The carbon fiber adhesive should store in a cool and dry place,storage period is 12 months. If storage period exceed 12 months, the product should be tested, if the physical and mechanical properties meet the standard requirements,you can still continue to use it.

• This product is non-toxic, belong to non-dangerous goods, transport as a goods, transport as a general chemical building materials

Transportation and Storage

• The carbon fiber adhesive should store in a cool and dry place,storage period is 12 months. If storage period exceed 12 months, the product should be tested, if the physical and mechanical properties meet the standard requirements,you can still continue to use it.

• This product is non-toxic, belong to non-dangerous goods, transport as a goods, transport as a general chemical building materials

carbon fiber adhesive for FRP strengthening

Attention Points

• Mix proper quantity, use up in the applicable period.

• If there is any left, the lids of A B should be covered. Do not expose it in the air.

• Construction workers should take certain protective measures.

• The construction environment should be kept ventilated during construction.

• Avoid direct sunlight and high temperature.

Attention Points

• Mix proper quantity, use up in the applicable period.

• If there is any left, the lids of A B should be covered. Do not expose it in the air.

• Construction workers should take certain protective measures.

• The construction environment should be kept ventilated during construction.

• Avoid direct sunlight and high temperature.

 

 

 

Horse Carbon Fiber Fabric Adhesive

HM-180C3P CFRP Fabric Epoxy TDS - Horse.pdf


Technical Parameters
AppearanceComponent A: viscous liquidPot life (min)≥60
Component B: viscous liquidOperating temperature℃5~40


Finger touch dry time(25℃, h)1~2
The basic properties after pasted carbon fiber cure
Standard value of tensile strength (MPa)≥38Ultimate elongation (%)≥1.5
Elastic modulus (MPa)≥2400Mixture ratioA:B=2:1
Elongation≥1.5%Thixotropic index≥3.0
Non-volatile matter content≥99%Distortion temperature≥65℃
Steel-steel adhesive tensile strength≥40MpaSteel - steel T impact stripping length≤20mm

Long-term performance

Wet and heat ageing 

resistance ability

Compared with the short-term results at room temperature,

the decrease rate of shear strength: ≤12%

Heat aging 

resistance

Compared with the short-term results at same temperature 10min,

the decrease rate of shear strength: ≤5%

Freezing and thawing 

resistance ability

Compared with room temperature, short-term results,

the shear strength decrease rate is not greater than 5%

Fatigue stress 

resistance ability

After2×106 times continuous sine wave fatigue loads, 

specimen does not destroy

Resistance to stress 

for a long time

Steel - steel tensile shear specimens does not destroy, 

and creep deformation value is less than 0.4 mm

Resistance to corrosion medium

Resistance to salt

 fog effect

Compared with the control group, the strength decrease rate: ≤5%,

and shall not have cracks or come unglued

Alkaline medium 

resistance ability

Compared with the control group, the strength does not decrease, 

and as the concrete damage, and shall not have cracks or come unglued

Acid medium 

resistance ability

Concrete damage, and shall not have cracks or degumming
The properties after carbon fiber cure
Colloidal performanceCompressive strength(MPa)≥70.0

Working

performance

Nonvertical mobility(mm), 30℃2.0
Tensile strength(MPa)≥40.0Operable time(min), 30℃>40
Bending Strength(MPa)≥50.0Applicable Temperature(℃)5~40
Elastic strength(MPa)≥2500
Bonding capacity

Steel-steel tensile shear strength(MPa)

≥14Mixing ratioA:B=2:1

Pulling bonding strength along

with concrete(MPa)

≥2.5Curing time(d),25℃3~7
Steel-concrete tensileC60 concrete damage


Horse HM-180C3P Carbon Fiber Adhesive 


Carbon Fiber Strengthening Video(click it)


>>The treatment of concrete surface
The cosmetic layer, oil, dirt etc. Of concrete surface should be chiseled off and then rubbed off 1 ~2 mm thick surface layer with the

angle grinder, concrete components should be handled by chamfering on the corner, dust was blew out with compressed air after the

completion Of polishing, and finally the surface was wiped by cotton cloth dipped in acetone, and kept dry for use. If the concrete

needed to strengthen existed cracks, first choose HM-120M perfusion adhesive or HM-120L pouring crack adhesive to perfuse according
to the size of crack, and then strengthen.

>>Primer construction
When construction, two components of HM-180 primer were weighed according to the stipulated proportion of preparing glue, and

dumped into a clean container and stirred to uniformity (when mixing, best mix along the same direction to avoid the air from forming

air bubbles.) Brush or roller brush was used to evenly brush on the concrete surface, after the glue surface layer dried, it should be

brushed several times depending on the particular circumstances, but the coating thickness did not exceed 0.4 mm, and it should
not be missed out to brush, or have flowing or bubbles, waiting for glue curing (curing time was depended on the site temperature,

it was appropriate when finger felt dry, generally not less than 2 hours), then the next process was proceeded. The glue prepared

every time should be used up one time during the applicable period of the glue.

 

>>Leveling construction
The pores and defects on concrete surface were filled by HM-180CE leveling adhesive.When depression area was existed, the prepared leveling

adhesive was used to repair and fill through scraper embedding and scraping, the position emerging altitude difference such as the

joint of templates should be filled by leveling adhesive, which tried to minimize the height difference. The treatment of corner was that

it was repaired to smooth arc through leveling adhesive, its radius was not more than 20mm. After the leveling adhesive cured (curing
time was depended on the site temperature, it was appropriate when finger felt dry, generally not less than 2 hours), the next process

should be proceeded further.

>>Paste of carbon fiber wrap

HM-180C3P carbon fiber impregnated adhesive was smeared to the pasted area evenly,the corner site was more smeared appropriately. Paste after

hauling carbon fiber wrap tight and alignment, use a plastic scraper or roller (a paint roller that the villus was removed outside) to roll

repeatedly along the same direction, until the glue compound exuded. And then smear impregnated adhesive to the outside surface

of the carbon fiber wrap evenly, and roll repeatedly that the impregnated adhesive can immerse the carbon fiber wrap in two ways,

if it is multi-paste, until your fingers touch dry, the next layer of paste can be beginner. If the carbon fiber wrap needs overlapping


>>Curing and conservation
Prevent rain or moisture 24 hours after the completion of construction, and pay attention to protection against a hard Object bumping

into the surface of the construction. When the average air temperature is 20 , 25 ℃ , the curing time is not less than 3 days; when

the average air temperature is 10 ℃, the curing time is not less than 7 days.

 